DIATOMITE INSULATING BRICK

кликнуть картину и смотреть оригинал
расценка: лично обсудить
минимальное количество заказа:
общее количество поставки:
срок отправки таваров: С момента оплаты покупателей с даты ,за 30 дней отправить тавары
местонахождение: Asia China
срок действия до: долгосрочная эффективность
время обновления последного раза: 2016-07-01 14:19
количество просмотра: 183
спрашиватьОтправить по электронной почте
основные информации компании
Tel: +86-411-62885583
Email: sales@cimmuk.com
Address: 2nd Floor, Zhiye Plaza, 135-137 Guangxian Road, Hi-Tech Industrial Park, Dalian, Liaoning 116085
Skype: Mark Ma
WhatsApp: +8618624286999
WeChat: 18624286999
 
 
подробное описание продукции
 It is produced by nature diatomite. The main features are higher apparent porosity, better insulating property, lower volume density, lower energy consume, smaller brick work thickness, lower project costs, improved work environment, higher productivity. It can use below 900℃. In addition, it is convenient to construct and lower.
--Application
v It is mostly applied heat preservation of pipeline transportation equipments of the gas and the liquid in electric power, metallurgy, engineering, chemical industry, petroleum industries etc. Also, it is used to the thermal protective coating of high temperature equipment within electric furnace, heating furnace, steel furnace, annealing furnace, and glass furnace etc.  
v For aluminium electrolytic pot, the diatomite insulating brick can be used for the masonry of pot bottom and lower portion of pot side wall along the length as heat insulating layer;
vFor bake oven, the diatomite insulating brick can be used for masonry of wall as heat insulating layer.

ITEM

Unit

CM-GG-0.7a

CM-GG-0.7b

CM-GG-0.6

CM-GG-0.5

TEST METHOD

Bulk Density ,                 ≤

g/cm3

0.75

0.7

0.6

0.55

GB/T2998-2001

(ISO 5016-1997)

Cold Crushing strength,

Mpa

1.8

1.2

0.8

0.8

GB/T5072-2008

(ISO 8895-2004)

Thermal conductivity,      ≤

W/m.k

GB/T5990-2008

(ISO 8894-2:1990)

At 2000C

0.20

0.20

0.17

0.17

At 4000C

0.23

0.23

0.19

0.19

At 6000C

0.25

0.25

0.21

0.21

Permanent Linear change after reheating at 9000C*8hrs,                     ≤

2.0

2.0

2.0

2.0

GB/T3997.1-1998

(ISO 2477-2005)

Tolerance of length

mm

±2

                     width

mm

±1

                     thickness

mm

±1

 
более»другие продукции нашей компании

[ поиск ]  [ добавить в папку ]  [ передать другу ]  [ печатать текст ]  [ закрыть окно ]


 